Ladd McCluskey December 6, 2021 Metals, LPBF 304L Stainless Steel Ladd McCluskey December 6, 2021 Metals, LPBF Corrosion resistant, weldable, machinable:Yield Stress: 430 MPa or 62.37 ksiUltimate Tensile Strength: 530 MPa or 76.87 ksiElongation: 32%
Ladd McCluskey December 6, 2021 Metals, LPBF 4340 Steel Ladd McCluskey December 6, 2021 Metals, LPBF Strong, ductile, heat treatable:Yield Strength: 1545 MPa or 224.08 ksiTensile Strength: 12.93 GPa or 1875 ksiElongation: 12%
Ladd McCluskey December 13, 2020 Carbon DLS, CLIP, Plastics RPU 70 Ladd McCluskey December 13, 2020 Carbon DLS, CLIP, Plastics Strong, rigid, flame rated, and chemical compatible:Tensile Strength: 40 MPa or 6 ksiTensile Modulus: 1700 MPa or 245 ksiFlexural Modulus: 1500 MPa or 220ksiElongation at Break: 30%Durometer (Shore D Hardness): 80
Ladd McCluskey December 13, 2020 3D Systems Figure 4, DLP, Plastics TOUGH-GRY 10 Ladd McCluskey December 13, 2020 3D Systems Figure 4, DLP, Plastics High speed prints:Tensile Strength: 50 MPa or 7.19 ksiTensile Modulus: 2180 MPa or 317 ksiFlexural Modulus: 2070 MPa or 300ksi
Ladd McCluskey December 13, 2020 3D Systems Figure 4, DLP, Plastics PRO-BLK 10 Ladd McCluskey December 13, 2020 3D Systems Figure 4, DLP, Plastics Similar to thermoplastics—strong, rigid, and fast build times:Tensile Strength: 63 MPa or 9.14 ksiTensile Modulus: 2320 MPa or 336 ksiFlexural Modulus: 2290 MPa or 332ksi
Ladd McCluskey December 12, 2020 3D Systems Figure 4, DLP, Plastics Rigid White Ladd McCluskey December 12, 2020 3D Systems Figure 4, DLP, Plastics Biocompatible and environmentally stable:Tensile Strength: 57 MPa or 8.2 ksiTensile Modulus: 2100 MPa or 300 ksiHeat Deflection: 65°C or 149°FElongation at Break: 20%
Ladd McCluskey December 12, 2020 3D Systems Figure 4, DLP, Plastics FLEX-BLK 20 Ladd McCluskey December 12, 2020 3D Systems Figure 4, DLP, Plastics Fatigue and impact resistant:Tensile Strength: 36 MPa or 5.22 ksiTensile Modulus: 840 MPa or 122 ksiElongation at Break: 86%Impact Strength (Notched): 91 J/m or 1.7 ft-lb/in
Ladd McCluskey December 11, 2020 Carbon DLS, CLIP, Plastics FPU 50 Ladd McCluskey December 11, 2020 Carbon DLS, CLIP, Plastics Semi-rigid with fatigue, impact, and abrasion resistance:Elongation at Break: 200%Durometer (Shore D Hardness): 71Tensile Strength: 25 MPa or 4 ksiTensile Modulus: 700 MPa or 100 ksi
Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics HP PA 11 Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics Strong, ductile, impact resistant:Tensile Strength: 52 MPa or 7.54 ksiTensile Modulus: 1800 MPa or 261 ksiFlexural Modulus: 1800 MPa or 261 ksiElongation at Break: 40% (ZX, ZY) and 25%
Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics HP PA 12 Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics Low-Cost, strong, chemical resistant, and watertight:Tensile Strength: 48 MPa or 6.96 ksiTensile Modulus: 1700 MPa or 247 ksiFlexural Modulus: 1730 MPa or 251 ksi
Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics HP PA 12 Glass Filled Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics Dimensional Stability and 40% Glass Beads:Tensile Strength: 30 MPa or 4.35 ksiTensile Modulus: 2800 MPa or 406 ksiHeat Deflection: 121° C or 250° F
Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics Polypropylene Ladd McCluskey December 11, 2020 HP Jet Fusion, MJF, Plastics Excellent plasticity with chemical resistance and low moisture absorption:Tensile Strength: 30 MPa or 4.35 ksiTensile Modulus: 1600 MPa or 232 ksiElongation at Break: 20% (ZX, ZY) and 18%Heat Deflection: 100° C or 212° F
Ladd McCluskey December 11, 2020 3D Systems Figure 4, DLP, Plastics TOUGH-BLK 20 Ladd McCluskey December 11, 2020 3D Systems Figure 4, DLP, Plastics High endurance material designed to mimic ABS injection molding:Tensile Strength: 40 MPa or 5.86 ksiTensile Modulus: 1780 MPa or 260 ksiElongation at Break: 36%
Ladd McCluskey December 10, 2020 Carbon DLS, CLIP, Plastics EPX 82 Ladd McCluskey December 10, 2020 Carbon DLS, CLIP, Plastics Comparable to glass-filled thermoplastics—high endurance and resistant:Tensile Strength: 80 MPa or 10 ksiTensile Modulus: 2800 MPa or 410 ksiHeat Deflection Temp: 115°C or 240°F
Ladd McCluskey December 10, 2020 3D Systems Figure 4, DLP, Plastics RUBBER-65A BLK Ladd McCluskey December 10, 2020 3D Systems Figure 4, DLP, Plastics Production elastomer with long-term stability:Tensile Strength: 5 MPa or .725 ksiTensile Modulus: 23 MPa or 3.3 ksiElongation at Break: 126%Durometer (Shore A Hardness): 65
Ladd McCluskey December 10, 2020 Carbon DLS, CLIP, Plastics EPU 40 Ladd McCluskey December 10, 2020 Carbon DLS, CLIP, Plastics Similar to rubber—both tear and impact resistant:Durometer (Shore A Hardness): 68Elongation at Break: 300%Tensile Strength: 9 MPa or 1300 psiTensile Modulus: 8 MPa or 1200 psi
Ladd McCluskey December 9, 2020 Carbon DLS, CLIP, Plastics UMA 90 Ladd McCluskey December 9, 2020 Carbon DLS, CLIP, Plastics Rigid, fast, colorful, and inexpensive:Tensile Strength: 30 MPa or 4.4 ksiTensile Modulus: 1400 MPa or 200 ksiDurometer (Shore D Hardness): 86
Ladd McCluskey December 8, 2020 Carbon DLS, CLIP, Plastics SIL 30 Ladd McCluskey December 8, 2020 Carbon DLS, CLIP, Plastics Soft, biocompatible, and flexible material:Durometer (Shore A Hardness): 35Tear Strength: 10 kN/m or 57 lbf/inElongation at Break: 350%
Ladd McCluskey December 8, 2020 Carbon DLS, CLIP, Plastics Whip Mix (WPMX) Ladd McCluskey December 8, 2020 Carbon DLS, CLIP, Plastics Clear and Biocompatible for Dental Applications:Elastic Modulus: 1700 MPa or 247 ksiElongation at Break: 10%Durometer (Shore D Hardness): 80
Ladd McCluskey December 8, 2020 HP Jet Fusion, MJF, Plastics TPU Ladd McCluskey December 8, 2020 HP Jet Fusion, MJF, Plastics Elastic and soft material:Tensile Strength: 11 MPa (XY) and 5 (Z)Elongation at Break: 180% (XY) and 30% (Z)Tear Strength: 80 kN/mm (XY) and 33 kN/mm (Z)Durometer (Shore A Hardness): 95