Corrosion resistant, weldable, machinable:

Yield Stress: 430 MPa or 62.37 ksi

Ultimate Tensile Strength: 530 MPa or 76.87 ksi

Elongation: 32%

Strong, ductile, heat treatable:

Yield Strength: 1545 MPa or 224.08 ksi

Tensile Strength: 12.93 GPa or 1875 ksi

Elongation: 12%

Strong, rigid, flame rated, and chemical compatible:

Tensile Strength: 40 MPa or 6 ksi

Tensile Modulus: 1700 MPa or 245 ksi

Flexural Modulus: 1500 MPa or 220ksi

Elongation at Break: 30%

Durometer (Shore D Hardness): 80

High speed prints:

Tensile Strength: 50 MPa or 7.19 ksi

Tensile Modulus: 2180 MPa or 317 ksi

Flexural Modulus: 2070 MPa or 300ksi

Similar to thermoplastics—strong, rigid, and fast build times:

Tensile Strength: 63 MPa or 9.14 ksi

Tensile Modulus: 2320 MPa or 336 ksi

Flexural Modulus: 2290 MPa or 332ksi

Biocompatible and environmentally stable:

Tensile Strength: 57 MPa or 8.2 ksi

Tensile Modulus: 2100 MPa or 300 ksi

Heat Deflection: 65°C or 149°F

Elongation at Break: 20%

Fatigue and impact resistant:

Tensile Strength: 36 MPa or 5.22 ksi

Tensile Modulus: 840 MPa or 122 ksi

Elongation at Break: 86%

Impact Strength (Notched): 91 J/m or 1.7 ft-lb/in

Semi-rigid with fatigue, impact, and abrasion resistance:

Elongation at Break: 200%

Durometer (Shore D Hardness): 71

Tensile Strength: 25 MPa or 4 ksi

Tensile Modulus: 700 MPa or 100 ksi

Strong, ductile, impact resistant:

Tensile Strength: 52 MPa or 7.54 ksi

Tensile Modulus: 1800 MPa or 261 ksi

Flexural Modulus: 1800 MPa or 261 ksi

Elongation at Break: 40% (ZX, ZY) and 25%

Low-Cost, strong, chemical resistant, and watertight:

Tensile Strength: 48 MPa or 6.96 ksi

Tensile Modulus: 1700 MPa or 247 ksi

Flexural Modulus: 1730 MPa or 251 ksi

Dimensional Stability and 40% Glass Beads:

Tensile Strength: 30 MPa or 4.35 ksi

Tensile Modulus: 2800 MPa or 406 ksi

Heat Deflection: 121° C or 250° F

Excellent plasticity with chemical resistance and low moisture absorption:

Tensile Strength: 30 MPa or 4.35 ksi

Tensile Modulus: 1600 MPa or 232 ksi

Elongation at Break: 20% (ZX, ZY) and 18%

Heat Deflection: 100° C or 212° F

High endurance material designed to mimic ABS injection molding:

Tensile Strength: 40 MPa or 5.86 ksi

Tensile Modulus: 1780 MPa or 260 ksi

Elongation at Break: 36%

Comparable to glass-filled thermoplastics—high endurance and resistant:

Tensile Strength: 80 MPa or 10 ksi

Tensile Modulus: 2800 MPa or 410 ksi

Heat Deflection Temp: 115°C or 240°F

Production elastomer with long-term stability:

Tensile Strength: 5 MPa or .725 ksi

Tensile Modulus: 23 MPa or 3.3 ksi

Elongation at Break: 126%

Durometer (Shore A Hardness): 65

Similar to rubber—both tear and impact resistant:

Durometer (Shore A Hardness): 68

Elongation at Break: 300%

Tensile Strength: 9 MPa or 1300 psi

Tensile Modulus: 8 MPa or 1200 psi

Rigid, fast, colorful, and inexpensive:

Tensile Strength: 30 MPa or 4.4 ksi

Tensile Modulus: 1400 MPa or 200 ksi

Durometer (Shore D Hardness): 86

Soft, biocompatible, and flexible material:

Durometer (Shore A Hardness): 35

Tear Strength: 10 kN/m or 57 lbf/in

Elongation at Break: 350%

Clear and Biocompatible for Dental Applications:

Elastic Modulus: 1700 MPa or 247 ksi

Elongation at Break: 10%

Durometer (Shore D Hardness): 80

Elastic and soft material:

Tensile Strength: 11 MPa (XY) and 5 (Z)

Elongation at Break: 180% (XY) and 30% (Z)

Tear Strength: 80 kN/mm (XY) and 33 kN/mm (Z)

Durometer (Shore A Hardness): 95

Heat and chemical resistant:

Tensile Strength: 92 MPa or 13 ksi

Tensile Modulus: 3870 MPa or 561 ksi

Heat Deflection Temp: 231°C or 448°F

Industry leader in ultra-high temperature resistance:

Tensile Strength: 81 MPa or 11.75 ksi

Tensile Modulus: 4000 MPa or 580 ksi

Heat Deflection: >300°C or >570°F